产品简介
不锈钢带 SUS301不锈钢带 SUS304不锈钢带-SUS631不锈钢带 可生产的规格是0.01-6.0mm，采用可逆式精轧机生产，朝展产品表面精度高，弹性强韧性足，常用于制作弹**如压力开关，温控器之类的。
产品详细信息
不锈钢带 SUS301不锈钢带 SUS304不锈钢带 的力学性能
|
朝展牌 号
|
朝展状态符号
|
朝展产品拉力试验
|
|
屈服强度
óo.2
／MPa≥
|
抗拉强度
ób
／MPa≥
|
伸长率δ5(％)≥
|
|
厚度
<O．4
|
厚度
≥O．4～0.8
|
厚度
>O．8
|
|
17-7PH
|
A
|
380
|
1030
|
20
|
|
DY
|
|
1080-1230↑
|
5
|
|
BY
|
|
1180-1420↑
|
|
|
Y
|
|
1420-1720↑
|
|
|
1Cr17Ni7
|
DY
|
510
|
865
|
25
|
25
|
25
|
|
BY
|
755
|
1030
|
9
|
10
|
10
|
|
Y
|
930
|
1205
|
3
|
5
|
7
|
|
TY
|
960
|
1275
|
3
|
4
|
5
|
|
0Cr18Ni9
SUS304
|
BY
|
|
785
|
20
|
20
|
20
|
|
Y
|
|
980
|
10
|
lO
|
10
|
|
TY
|
|
1130
|
5
|
5
|
5
|
|
1Cr18Ni9Ti
SUS321
|
BY
|
|
735
|
20
|
20
|
20
|
|
Y
|
|
885
|
7
|
7
|
7
|
|
3CR13
420
|
A
|
|
|
|
|
|
|
淬火回火
|
540
|
735
|
12
|
厚度允许偏差 (mm)
|
朝展产品厚度
|
朝展产品宽 度
|
|
20～150
|
>150～250
|
>250～400
|
>400～600
|
|
0.05～0.10
|
±0.010
|
±0.010
|
±0.010
|
±0.010
|
|
>0.10～0.15
|
±0.010
|
±0.010
|
±0.010
|
±0.010
|
|
>0.15～0.25
|
±0.010
|
±0.010
|
±0.010
|
±0.010
|
|
>0.25～0.45
|
±0.020
|
±0.020
|
±0.020
|
±0.020
|
|
>0.45～0.65
|
±0.020
|
±0.020
|
±0.020
|
±0.020
|
|
>0.65～0.90
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>0.90～1.20
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>1.20～1.50
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>1.50～1.80
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>1.80～2.00
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>2.00-2.30
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>2.30～2.50
|
±0.030
|
±0.030
|
±0.030
|
±0.030
|
|
>2.50～3.10
|
±0.040
|
±0.040
|
±0.040
|
±0.040
|
|
>3.10～<4.00
|
±0.040
|
±0.040
|
±0.040
|
±0.040
|
切边钢带宽度上等精度(K)的允许偏差 (mm)
|
朝展产品厚度
|
朝展产品宽 度
|
|
20～150
|
>150～250
|
>250～400
|
>400～600
|
>600～1000
|
|
0.05～0.50
|
±0.10
|
±0.10
|
±0.15
|
±0.15
|
±0.15
|
|
>0.50～1.00
|
±0.10
|
±0.10
|
±0.15
|
±0.15
|
±0.15
|
|
>1.00～1.50
|
±0.10
|
±0.10
|
±0.15
|
±0.15
|
±0.15
|
|
>1.50～2.50
|
±0.10
|
±0.10
|
±0.15
|
±0.15
|
±0.15
|
|
>2.50～4.00
|
±0.10
|
±0.10
|
±0.15
|
±0.15
|
±0.15
|
|
朝展牌 号
|
朝展化学成分(质量分数)(％)
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni
|
Cr
|
M0
|
其他
|
|
奥氏体型
|
|
1Cr17Ni7
|
≤0.15
|
≤1.00
|
≤2.00
|
≤0.035
|
≤O.030
|
6.00～8.00
|
16.00～18.00
|
|
|
|
OCrl8Ni9
|
≤0.07
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
8.00～11.00
|
17.00～19.00
|
|
|
|
OCr25Ni20
|
≤O.08
|
≤1.00
|
≤2.00
|
≤O.035
|
≤0.030
|
19.00～22.00
|
24.00～26.00
|
|
|
|
OCr17Ni12M02
|
≤0.08
|
≤1.00
|
≤2.00
|
≤O.035
|
≤O.030
|
10.00～14.00
|
16.00～18.50
|
2.00～3.00
|
|
|
00Crl7Ni14M02
|
≤0.030
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
12.00～15.oo
|
16.00～18.00
|
2.00～3.00
|
|
|
lCrl8Ni9Ti⑥
|
≤0.12
|
≤1.00
|
≤2.00
|
≤O.035
|
≤O.030
|
8.00～11.00
|
17.00～19.00
|
|
Ti5×(C％-O.02)～O.80
|
|
铁素体型
|
|
1Cr17
|
≤ O.12
|
≤O.75
|
≤1.00
|
≤O.035
|
≤O.030
|
③
|
16.00～18.00
|
|
|
|
马氏体型
|
|
1Cr13
|
≤ O.15
|
≤1.00
|
≤1.00
|
≤0.035
|
≤O.030
|
③
|
13.50～11.50
|
|
|
|
0Cr13
|
≤O.08
|
≤1.00
|
≤1.00
|
≤O.035
|
≤O.030
|
③
|
13.50～
11.50
|
|
|
|
|
0.16 ～O.25
|
≤1.00
|
≤1.00
|
≤O.035
|
≤O.030
|
③
|
12.00～14.00
|
|
|
|
3Cr13
|
O.26～
O.35
|
≤1.00
|
≤1.00
|
≤O.035
|
≤O.030
|
③
|
12.00～14.00
|
|
|
|
4Cr13
|
0.36～
O.45
|
≤O.60
|
≤0.80
|
≤O.035
|
≤0.030
|
③
|
12.00～
14.00
|
|
|
|
1Cr17N2
|
0.11～0.17
|
≤O.80
|
≤O.80
|
≤0.035
|
≤O.030
|
1.50～2.50
|
16.00～18.00
|
|
|
|
7Cr17
|
O.60～
O.75
|
≤1.00
|
≤1.00
|
≤0.035
|
≤O.030
|
③
|
16.00～18.00
|
①
|
|
|
9Crl8
|
0.90～
1.00
|
≤O.80
|
≤0.80
|
≤O.035
|
≤0.030
|
③
|
17.00～19.00
|
④
|
|
|
9Cr18Mo
|
O.95～
1.10
|
≤0.80
|
≤O.80
|
≤O.035
|
≤0.030
|
③
|
16.00～18.00
|
0.40～0.70
|
|
|
9Cr18MoV
|
O.85～
0.95
|
≤O.80
|
≤0.80
|
≤O.035
|
≤O.030
|
③
|
17.00～19.00
|
1.00～
1.30
|
V0.07
～O.012
|
|
沉淀硬化型
|
|
OCr17NI4Cu4Nb
|
≤O.07
|
≤1.00
|
≤1.00
|
≤0.035
|
≤O.030
|
3.00～5.00
|
15.50～17.50
|
Cu3.00～5.00
|
Nb0.15～O.45
|
|
|
≤0.09
|
≤I.00
|
≤1.00
|
≤O.035
|
≤0.030
|
6.50～7.75
|
16.00～18.00
|
Cu≤O.50
|
A10.75～1.50
|
|
0Cr15Ni7M02Al
|
≤0.09
|
≤1.00
|
≤1.00
|
≤O.035
|
≤O.030
|
6.50～7.50
|
14.00～16.00
|
2.00～3.00
|
A10.75～1.50
|
经热处理的沉淀硬化型钢的力学性能
|
朝展牌号
|
热处理／℃
|
朝展产品拉伸试验
|
硬度试验
|
|
种类
|
条 件
|
óo.2
|
ób
|
δ5 (％)
≥
|
Ψ (％)≥
|
布氏硬度HBS
|
洛氏硬度
HRC
|
|
MPa
|
|
|
固溶
|
1020～1060
快冷
|
|
|
|
|
≤363
|
≤38
|
|
480时效
|
经固溶处理后，470～490空冷
|
≥180
|
≥ 1310
|
10
|
40
|
≥375
|
≥40
|
|
550时效
|
经固溶处理后，540～560空冷
|
≥000
|
≥ 1060
|
12
|
45
|
≥331
|
≥35
|
|
580时效
|
经固溶处理后，
570～590空冷
|
≥865
|
≥ 1000
|
13
|
45
|
≥302
|
≥31
|
|
620时效
|
经固溶处理后，
610～630空冷
|
≥725
|
≥930
|
16
|
50
|
≥277
|
≥28
|
|
0Cr17Ni7A1
|
固溶
|
1000～1100快冷
|
≤380
|
≤1030
|
20
|
|
≤229
|
|
|
565时效
|
①
|
≤960
|
≥1140
|
5
|
25
|
≥363
|
|
|
565时效
|
②
|
≤1030
|
≥1230
|
4
|
lO
|
≥388
|
|
|
OCr15Ni7M02A1
|
固溶
|
1000～1100快冷
|
|
|
|
|
≤269
|
|
|
565时效
|
①
|
≥1100
|
≥1210
|
7
|
25
|
≥375
|
|
|
510时效
|
②
|
≥ 1210
|
≥1320
|
6
|
20
|
≥388
|
|
不锈钢的特性和应用
|
类型
|
牌 号
|
朝展产品特性和应用
|
|
奥氏
体铁素体型
|
|
经冷加工有高的强度，铁道车辆，传送带螺栓螺母用
|
|
0Cr18Ni9
|
作为不锈耐热钢使用广泛，如食品用设备，一般化工设备，原子能工业用设备
|
|
0Cr25Ni20
|
抗氧化性比0Cr23Ni13好，实际上多作为耐热钢使用
|
|
0Cr17Ni12Mo2
|
在海水和其他各种介质中，耐腐蚀性比0Cr19Ni9好，主要作耐点蚀材料
|
|
00Cr17Ni14Mo2
|
为0Cr17Ni12Mo2的超低碳钢，比0Cr17ni14mo2耐晶问腐蚀性好
|
|
1Cr18Ni9Ti
|
作焊芯、抗磁仪表、医疗器械、耐酸容器及设备衬里输送管道等设备和零件
|
|
铁素体
|
1Cr17
|
耐蚀性良好的通用钢种，建筑内装饰用，重油燃烧器部件，家庭用具，家用电器部件
|
|
马氏
体型
|
1Cr13
|
朝展产品具有良好的耐蚀性，机械加工性，一般用途，刃具类
|
|
0Cr13
|
作较高韧性及受冲击负荷的零件，如汽轮机叶片、结构类、不锈设备、衬里、螺栓、螺母等
|
|
Y1C13
|
朝展不锈钢中切削性能*好的钢种，自动车床用
|
|
2Cr13
|
淬火状态下硬度高，耐蚀性良好，作汽轮机叶片
|
|
3Cr13
|
比2Cr13淬火后硬度高，作刃具、喷嘴、阀座、阀门等
|
|
4Cr13
|
作较高硬度及高耐磨性的热油泵轴、阀片、阀门轴承、医疗器械、弹簧等零件
|
|
1Cr17Ni2
|
具有较高强度的耐硝酸及有机酸腐蚀的零件、容器和设备
|
|
7Cr17
|
硬化状态下，坚硬，但比8Cr17、11Cr17韧性高。作刃具、量具、轴承
|
|
8Cr17
|
硬化状态下，比7Cr17硬，而比11Cr17韧性高。作刃具、阀门
|
|
9C18
|
不锈切片机械刃具及剪切刀具、手术刀片、高耐磨设备零件等
|
|
9Cr18Mo
|
轴承套圈及滚动体用的高碳铬不锈钢
|
|
9Cr18MoV
|
不锈切片机械刃具及剪切工具、手术刀片、高耐磨设备零件等
|
|
沉淀
硬化
型
|
0Cr17Ni4Cu4Nb
|
朝展添加铜的沉淀硬化型钢种。轴类、汽轮机部件
|
|
|
添加铝的沉淀硬化型钢种，作弹簧、热圈、计器部件
|
|
0Cr15Ni7Mo2AL
|
用于有一定耐蚀要求的高强度容器、零件及结构件
|